产品名称
钛, wire reel, 1m, diameter 0.5mm, as drawn, 99.99+%
InChI
1S/Ti
SMILES string
[Ti]
InChI key
RTAQQCXQSZGOHL-UHFFFAOYSA-N
assay
99.99%
form
wire
autoignition temp.
860 °F
manufacturer/tradename
Goodfellow 166-027-68
resistivity
42.0 μΩ-cm, 20°C
L × diam.
1 m × 0.5 mm
bp
3287 °C (lit.)
mp
1660 °C (lit.)
density
4.5 g/mL at 25 °C (lit.)
General description
For updated SDS information please visit www.goodfellow.com.
Legal Information
Product of Goodfellow
法规信息
新产品
此项目有
Wei-Qiang Yu et al.
Journal of nanoscience and nanotechnology, 14(6), 4387-4393 (2014-04-18)
The TiO2 nanotubes by anodization have been extensively studied for medical implant and orthopedic applications because of enhancing bone development. In the present study, a new nano-foveolae structure verified by SEM and AFM was prepared by simulating the nanotubes exfoliation
Bijuan Zheng et al.
Journal of nanoscience and nanotechnology, 14(5), 3527-3531 (2014-04-17)
Pd-modified N-doped TiO2 nanoparticles were prepared by the sol-gel method. The X-ray diffraction (XRD) pattern indicated that the pure anatase TiO2 has been obtained. Transmission electron microscope (TEM) was used to observe the micro-morphology of the nanoparticles. The average size
Konstantinos X Michalakis et al.
The Journal of oral implantology, 40(2), 146-152 (2014-05-02)
Dental implants with an internal connection have been designed to establish a better stress distribution when lateral external forces act on the prosthesis and minimize the forces transmitted to the fastening screw. In the present study, 10 externally and 10
P F Du et al.
Journal of nanoscience and nanotechnology, 14(6), 4164-4169 (2014-04-18)
Novel TiO2 nanoparticles/nanofibers (NPs/NFs) bilayered nano-composite photoanode film for dye-sensitized solar cells (DSSCs) was fabricated through the combination of spin-coating and electrospinning. The NPs and NFs layers have complementary roles. The underlaid spin-coated NPs layer provides the photoanode film with
Nikiwe Mhlanga et al.
Journal of nanoscience and nanotechnology, 14(6), 4269-4277 (2014-04-18)
This study reports the synthesis, characterisation and thermal properties of polylactide (PLA)/titanium dioxide nanoparticles (TiO2 NPs) composites using the sol-gel method. The percentage weight of TiO2 NP sol was varied from 3, 8, 11 and 14. The synthesised composites were
我们的科学家团队拥有各种研究领域经验，包括生命科学、材料科学、化学合成、色谱、分析及许多其他领域.
联系客户支持