Electro-catalytic activity of palladium modified nitrogen doped titania nanoparticles.

Electro-catalytic activity of palladium modified nitrogen doped titania nanoparticles.

Journal of nanoscience and nanotechnology (2014-04-17)

Bijuan Zheng, Bei Qi, Yulong Hu, Fan Zhang, Hongfang Liu

摘要

Pd-modified N-doped TiO2 nanoparticles were prepared by the sol-gel method. The X-ray diffraction (XRD) pattern indicated that the pure anatase TiO2 has been obtained. Transmission electron microscope (TEM) was used to observe the micro-morphology of the nanoparticles. The average size of the particles was 8.04 nm. The N2 adsorption isotherm of the resulted nanoparticles was the type IV with a H1 type hysteresis loop. The specific surface area was 145.2 m2 g(-1) and the average diameter of adsorption was 4.178 nm. These Pd-modified N-doped TiO2 nanoparticles were applied onto the surface of glass carbon electrode (GCE), and its electro-catalytic activity was tested by cyclic voltammetry (CV). The reduction peak currents showed a linear response to the dissolved oxygen (DO) concentrations ranging from 0.6 mg L(-1) to 7.2 mg L(-1) on the Pd-N-TiO2/ GCE. The linear regression equation was y = 3E - 6x + 1E-5 (R = 0.9909). The detection limit was 0.22 mg L(-1.) The result indicated that the Pd-N-TiO2 possessed a good electro-catalytic activity.

材料

货号

品牌

产品描述

GF29374005

钛, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh

GF16031843

钛, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

GF31127712

钛, rod, 10mm, diameter 50mm, 99.99+%

348864

Sigma-Aldrich

钛, wire, diam. 0.5 mm, 99.99% trace metals basis

GF46592949

钛, wire, straight, 1000mm, diameter 1.0mm, as drawn, 99.6+%

GF66682288

钛, wire reel, 100m, diameter 0.5mm, as drawn, 99.6+%

GF76772391

钛, rod, 100mm, diameter 10mm, annealed, 99.6+%

GF29584187

钛, tube, 500mm, outside diameter 2.03mm, inside diameter 1.55mm, wall thickness 0.24mm, annealed, 99.6+%

GF80932822

钛, wire reel, 0.5m, diameter 0.5mm, as drawn, 99.99+%

GF49264713

钛, tube, 200mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF16213553

钛, wire reel, 10m, diameter 0.125mm, annealed, 99.6+%

GF86399106

钛, tube, 500mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF17799777

钛, rod, 100mm, diameter 40mm, annealed, 99.6+%

GF90963928

钛, rod, 25mm, diameter 50mm, 99.99+%

GF33302832

钛, wire reel, 1m, diameter 1.0mm, annealed, 99.6+%

GF13900205

钛, tube, 100mm, outside diameter 0.51mm, inside diameter 0.35mm, wall thickness 0.08mm, annealed, 99.6+%

GF95731960

钛, tube, 500mm, outside diameter 3.0mm, inside diameter 1.5mm, wall thickness 0.75mm, annealed, 99.6+%

GF38954076

钛, rod, 200mm, diameter 6mm, annealed, 99.6+%

GF82495198

钛, rod, 200mm, diameter 9.5mm, annealed, 99.99+%

GF36846434

钛, wire reel, 100m, diameter 0.125mm, annealed, 99.6+%

GF62676759

钛, rod, 200mm, diameter 2mm, as drawn, 99.99+%

GF42959661

钛, tube, 1000mm, outside diameter 10mm, inside diameter 8mm, wall thickness 1.0mm, annealed, 99.6+%

GF14377631

钛, wire reel, 25m, diameter 0.25mm, annealed, 99.6+%

GF70333376

钛, wire reel, 10m, diameter 0.05mm, hard, 99.8%

GF04311638

钛, rod, 100mm, diameter 6mm, annealed, 99.6+%

GF54978249

钛, rod, 200mm, diameter 4mm, annealed, 99.6+%

GF20882998

钛, rod, 200mm, diameter 5mm, annealed, 99.6+%

GF21200746

钛, tube, 100mm, outside diameter 0.81mm, inside diameter 0.61mm, wall thickness 0.1mm, as drawn, 99.6+%

GF89377701

钛, tube, 100mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%

GF78234521

钛, wire reel, 1m, diameter 0.25mm, annealed, 99.6+%