Corrosion behavior of tantalum-coated cobalt-chromium modular necks compared to titanium modular necks in a simulator test.

Corrosion behavior of tantalum-coated cobalt-chromium modular necks compared to titanium modular necks in a simulator test.

The Journal of arthroplasty (2013-10-09)

Ulrich Dorn, Daniel Neumann, Mario Frank

摘要

This study compared the corrosion behavior of tantalum-coated cobalt-chromium modular necks with that of titanium alloy modular necks at their junction to titanium-alloy femoral stem. Tests were performed in a dry assembly and two wet assemblies, one contaminated with calf serum and the other contaminated with calf serum and bone particles. Whereas the titanium modular neck tested in the dry assembly showed no signs of corrosion, the titanium modular necks tested in both wet assemblies showed marked depositions and corrosive attacks. By contrast, the tantalum-coated cobalt-chromium modular necks showed no traces of corrosion or chemical attack in any of the three assemblies. This study confirms the protective effect of tantalum coating the taper region of cobalt-chromium modular neck components, suggesting that the use of tantalum may reduce the risk of implant failure due to corrosion.

材料

货号

品牌

产品描述

Sigma-Aldrich

钽, powder, −325 mesh, 99.9% trace metals basis

Sigma-Aldrich

钽

Sigma-Aldrich

钽, foil, thickness 0.025 mm, ≥99.9% trace metals basis

Sigma-Aldrich

钽, foil, thickness 0.25 mm, ≥99.9% trace metals basis

Sigma-Aldrich

钽, foil, thickness 0.05 mm, ≥99.9% trace metals basis

Sigma-Aldrich

钽, powder, 60-100 mesh, 99.9%

Sigma-Aldrich

钽, wire, diam. 1.0 mm, ≥99.9% trace metals basis

钽, foil, 50x50mm, thickness 0.5mm, annealed, 99.9%

钽, foil, 100x100mm, thickness 1.0mm, annealed, 99.9%

Sigma-Aldrich

钽, foil, thickness 0.5 mm, ≥99.9% trace metals basis

钽, foil, 100x100mm, thickness 0.25mm, annealed, 99.9%

钽, foil, light tested, 150x150mm, thickness 0.05mm, annealed, 99.9%

Sigma-Aldrich

钽, foil, thickness 1.0 mm, ≥99.9% trace metals basis

钽, rod, 100mm, diameter 1.0mm, 99.9%

钽, mesh, 100x100mm, nominal aperture 0.43mm, wire diameter 0.075mm, 50x50 wires/inch, open area 72%, plain weave mesh

钽, pellets, 50g, max. size 10mm, 99.9%

钽, foil, 100x100mm, thickness 0.100mm, annealed, 99.9%

钽, foil, 100x100mm, thickness 0.125mm, annealed, 99.9%

钽, mesh, 40x40mm, nominal aperture 0.43mm, wire diameter 0.075mm, 50x50 wires/inch, open area 72%, plain weave mesh

钽, sphere, 100pcs, diameter 1.0mm, precision sphere grade, 99.9%

钽, tube, 100mm, outside diameter 7.0mm, inside diameter 6.7mm, wall thickness 0.15mm, as drawn, 99.9%

钽, foil, 50x50mm, thickness 6.0mm, 99.9%

钽, foil, light tested, 100x100mm, thickness 0.025mm, as rolled, 99.9%

钽, rod, 100mm, diameter 3.0mm, annealed, 99.9%

钽, foil, 150x150mm, thickness 0.100mm, annealed, 99.9%

钽, wire reel, 1m, diameter 0.8mm, annealed, 99.9%

钽, foil, light tested, 100x100mm, thickness 0.03mm, as rolled, 99.9%

钽, foil, light tested, 100x100mm, thickness 0.05mm, annealed, 99.9%

钽, foil, light tested, 25x25mm, thickness 0.05mm, annealed, 99.9%

钽, foil, not light tested, 25x25mm, thickness 0.004mm, 99.9%