推荐产品
检测方案
99.99% trace metals basis
硬度
8.0 mohs
尺寸
10 mm × 10 mm × 0.5 mm
mp
2130 °C (lit.)
密度
3.64 g/mL at 25 °C (lit.)
半导体性质
<110>
SMILES字符串
[Mg++].[O-][Al]=O.[O-][Al]=O
InChI
1S/2Al.Mg.4O/q;;+2;;;2*-1
InChI key
VPBIQXABTCDMAU-UHFFFAOYSA-N
正在寻找类似产品? 访问 产品对比指南
应用
用于次锕系元素（例如镅）嬗变的惰性基质。
特点和优势
用于大型微波和声波设备的透明基板。III-V 氮化物材料的良好基板。
物理属性
传播损耗：6.5dB/μs；相速度：在（100> 剪切波）处为 6500m/x；热膨胀：7.45×10-6/°C
外形
立方晶系 (a = 8.083Å)
警示用语：
Warning
危险声明
危险分类
Eye Irrit. 2 - Skin Irrit. 2 - STOT SE 3
靶器官
Respiratory system
WGK
WGK 3
闪点(°F)
Not applicable
闪点(°C)
Not applicable
个人防护装备
Eyeshields, Gloves, type N95 (US)
法规信息
新产品
Satit Puttipipatkhachorn et al.
International journal of pharmaceutics, 293(1-2), 51-62 (2005-03-22)
Diclofenac calcium-alginate (DCA) beads were reinforced with different amounts of sodium starch glycolate (SSG) or magnesium aluminum silicate (MAS) and were prepared using ionotropic gelation method. Complex formation of sodium alginate (SA) and SSG or MAS in calcium-alginate beads was
J C Keller et al.
Dental materials : official publication of the Academy of Dental Materials, 13(1), 62-68 (1997-01-01)
The objective of this work was to examine osteoblast-like cell attachment and morphology in vitro to osteoceramic materials with three different surface morphologies. Osteoceramic composite disks were fabricated from tricalcium phosphate and magnesium-aluminate spinel (MgAl2O4) in a 50 vol% ratio.
Tomohito Kameda et al.
Chemosphere, 73(5), 844-847 (2008-07-25)
Magnesium-aluminum oxide (Mg-Al oxide) obtained by thermal decomposition of Mg-Al layered double hydroxide (Mg-Al LDH) effectively removed HCl from gaseous streams. HCl removal was greater in the presence of added water vapor at all temperatures examined and increased with decreasing
Klaassen, F.C.
J. Nuc. Mat., 319, 108-108 (2003)
Liang Lv et al.
Journal of hazardous materials, 152(3), 1130-1137 (2007-09-14)
A fundamental investigation on the uptake of bromide ion from contaminated water by calcined and uncalcined MgAl-CO3 layered double hydroxides (LDHs) were conducted in batch mode. The uptake capacity of calcined LDHs (CLDH) is higher than that of uncalcined LDHs
商品
Spintronics offer breakthroughs over conventional memory/logic devices with lower power, leakage, saturation, and complexity.
Synthesis of Melting Gels Using Mono-Substituted and Di-Substituted Alkoxysiloxanes
我们的科学家团队拥有各种研究领域经验，包括生命科学、材料科学、化学合成、色谱、分析及许多其他领域.
联系技术服务部门