所有图片(1)
About This Item
线性分子式:
CH2=CHSO3Na
CAS号:
分子量:
130.10
Beilstein:
3711195
MDL编号:
UNSPSC代码:
12162002
PubChem化学物质编号:
NACRES:
NA.23
推荐产品
等级
technical grade
包含
100 ppm monomethyl ether hydroquinone as inhibitor
浓度
25 wt. % in H2O
折射率
n20/D 1.376
密度
1.176 g/mL at 25 °C
SMILES字符串
[Na+].[O-]S(=O)(=O)C=C
InChI
1S/C2H4O3S.Na/c1-2-6(3,4)5;/h2H,1H2,(H,3,4,5);/q;+1/p-1
InChI key
BWYYYTVSBPRQCN-UHFFFAOYSA-M
应用
乙烯基磺酸钠是合成聚阴离子聚合物和共聚物的有效试剂（单体）。
储存分类代码
10 - Combustible liquids
WGK
WGK 1
闪点(°F)
Not applicable
闪点(°C)
Not applicable
个人防护装备
Eyeshields, Gloves, multi-purpose combination respirator cartridge (US)
Lars Gabriel et al.
Carbohydrate polymers, 246, 116533-116533 (2020-08-05)
The heterogeneous sulfoethylation of cellulose, xylan, α-1,3-glucan, glucomannan, pullulan, curdlan, galactoglucomannan, and agarose was studied using sodium vinylsulfonate (NaVS) as reagent in presence of sodium hydroxide and iso-propanol (i-PrOH) as slurry medium. The influence of the concentration of polymer, water
Yan-Fang Guan et al.
Water research, 185, 116203-116203 (2020-07-31)
Organic fouling and inorganic scaling are the main hurdles for efficient operation of reverse osmosis (RO) technology in a wide range of applications. This study demonstrates dual-functionality surface modification of thin-film composite (TFC) RO membranes to simultaneously impart anti-scaling and
Tri Quang Bui et al.
Polymers, 13(4) (2021-03-07)
Hydrogels can be utilized to extract energy from salinity gradients when river water mixes with seawater. Saline-sensitive hydrogels exhibit a reversible swelling/shrinking process when they are, alternately, exposed to fresh and saline water. We present a comparison of several poly(acrylic
Attempts at desensitization of women immunized by the Rh factor. I. The use of ethylene disulfonate.
W C MOLONEY
American journal of obstetrics and gynecology, 60(3), 616-625 (1950-09-01)
Semra Kirboğa et al.
Colloids and surfaces. B, Biointerfaces, 78(2), 357-362 (2010-04-20)
In this study, the effect of water soluble homopolymer of vinylsulfonic acid on spontaneous crystallization of calcium oxalate (CaOx) was investigated. CaOx crystals exhibiting different shapes and phase structures were produced in the presence of polymer. While the crystal growth
我们的科学家团队拥有各种研究领域经验，包括生命科学、材料科学、化学合成、色谱、分析及许多其他领域.
联系技术服务部门